VENTURELITE® 2050 is an aluminium honeycomb panel with decorative laminate faces reinforced with aluminium sheet

Strain-hardened hexagonal cell aluminium honeycomb has optimum mechanical properties and is able to carry shear loads at much lower weight than foam or other core types.

Minimal content of combustible materials means a low fire load, enabling VENTURELITE® 2050 to achieve flame spread test requirements.

  • Properties
  • Colours
  • Application
  • Processing
Properties

Properties

Panels are produced with the same decorative laminate on both faces, or with a backing/lining laminate on the reverse face Decorative faces are reinforced with aluminium sheet. A broad range of reinforcement sheet thicknesses are available, including 0.3mm, 0.5mm, 0.8mm and 1.0mm. 0.5mm is the standard reinforcement thickness. Aluminium reinforcement sheets can be selected with different thicknesses on different faces: for example, 0.8mm for front face, 0.3mm for back face. Aluminium reinforcement sheets are 5000-series alloy for maximum strength and anti-corrosion performance Aluminium honeycomb cell size is 6.35mm.

Metric

PHYSICAL AND MECHANICAL PERFORMANCE

Thickness Weight Long Beam Flatwise Tensile Flatwise Compression
(mm)
(kg/m2)
Max Load
(Newtons)
Deflection
at Max Load
(mm)
(MPa)
(MPa)
10 4.7 1379 21 1.2 2.6
20 5.3 2697 9 1.2 2.6
30 5.8 3695 7 1.2 2.6
Typical room temperature properties for 0.5mm aluminium faced panels. Mechanical test procedures to AMS-STD-401.

AVAILABILITY

Standard Dimensions
2400mm x 1200mm
Panel Thickness
Made to order, minimum thickness 6mm
Colours

Colours

Download Unleash your imagination Colour Chart

Unleash your imagination

Snow Flake
ACL101

Ivory
ACL113

Silver Lightning
ACL104

Odyssey
ACL106

Night Flight
ACL107

Platinum
ACL303

Crema Limestone
ACL204

Anthracite Granit
ACL205

Light Atelier
ACL206

Maple
ACL220

Bavaria Beech
ACL221

Cherry
ACL222

Amber Urban Oak
ACL223

Walnut
ACL224

Carbon Marine Wood
ACL225

Colours may vary by individual computer monitor from the actual final laminate product. We advise that the final selection is made from an actual sample.

Request a sample

Application

Application

Processing

Processing